Effects of notch root radius and stress ratio on the fatigue crack propagation threshold for the short crack at the notch root

The crack growth threshold, K th , for the short crack at the root of a long notch including the effects of notch root radius,  and stress ratio, R, were investigated in this study.The pre-crack, with a depth of 0.15mm, was introduced at the root of a 2mm deep notch which had the root radius chan...

Disgrifiad llawn

Manylion Llyfryddiaeth

Cyhoeddwyd yn:	Gruppo Italiano Frattura Digital Repository (Gruppo Italiano Frattura)
Prif Awduron:	Akimitsu Seo, Masanobu KUBOTA, Yoshiyuki Kondo
Fformat:	Erthygl
Iaith:	Saesneg
Cyhoeddwyd:	2012
Pynciau:	Fatigue and fracture mechanics Hydrogen embrittlement and corrosion behaviors in metals Mechanical Behavior of Composites fatigue crack growth crack growth threshold notch radius stress ratio short cracks crack closure unloading compliance method notch root
Mynediad Ar-lein:	http://www.gruppofrattura.it/ocs/index.php/esis/ECF19/paper/view/8943
Tagiau:	Ychwanegu Tag Dim Tagiau, Byddwch y cyntaf i dagio'r cofnod hwn!