Experimental investigations on the growth of small fatigue cracks in naval steel

ABSTRACT The concept of damage tolerance is now largely employed to evaluate the fatigue life of structures. However, part of this fatigue relies on the initiation and growth of small cracks. The fatigue behaviour of a naval structural steel (S355NL) was investigated. In order to characterize the be...

Descripció completa

Dades bibliogràfiques

Publicat a:	Fatigue & Fracture of Engineering Materials & Structures
Autors principals:	Aboulghit El Malki Alaoui, David Thévenet, A. Zeghloul
Format:	Article
Idioma:	anglès
Publicat:	Wiley 2007
Matèries:	Fatigue and fracture mechanics Mechanical Behavior of Composites Hydrogen embrittlement and corrosion behaviors in metals fatigue crack growth short fatigue cracks crack initiation crack propagation damage tolerance constant amplitude loading stress ratio fatigue life
Accés en línia:	https://onlinelibrary.wiley.com/doi/pdfdirect/10.1111/j.1460-2695.2007.01116.x https://doi.org/10.1111/j.1460-2695.2007.01116.x
Etiquetes:	Afegir etiqueta Sense etiquetes, Sigues el primer a etiquetar aquest registre!