Corrosion behavior of wrought magnesium alloys AZ31 and AZ61 in Hank’s solution
Abstract Corrosion behavior of wrought magnesium alloys AZ31 and AZ61 was studied in Hank’s solution. Potentiodynamic curves measured after short-term of exposure showed higher corrosion resistance of AZ31 magnesium alloy in comparison with AZ61 magnesium alloy. On the contrary, long-term tests meas...
Na minha lista:
| Publicado no: | Koroze a ochrana materialu |
|---|---|
| Main Authors: | , , , , , , |
| Formato: | Artigo |
| Idioma: | inglês |
| Publicado em: |
De Gruyter Open
2016
|
| Assuntos: | |
| Acesso em linha: | https://content.sciendo.com/downloadpdf/journals/kom/60/4/article-p101.pdf https://doi.org/10.1515/kom-2016-0016 |
| Tags: |
Sem tags, seja o primeiro a adicionar uma tag!
|
Registos relacionados: Corrosion behavior of wrought magnesium alloys AZ31 and AZ61 in Hank’s solution
- Influence of the Composition of the Hank’s Balanced Salt Solution on the Corrosion Behavior of AZ31 and AZ61 Magnesium Alloys
- Conversion Coatings Produced on AZ61 Magnesium Alloy by Low-Voltage Process
- Very high cycle fatigue of wrought magnesium alloy AZ61
- Improvement of corrosion resistance of AZ61 magnesium alloy / Zvýšení korozní odolnosti hořčíkové slitiny AZ61
- Near‐threshold fatigue crack growth properties of wrought magnesium alloy AZ61 in ambient air, dry air, and vacuum
- Methodology for In Situ Microstructural Characterisation of AZ31 Magnesium Alloy Corrosion Degradation in Hanks' Solution