Cracking Behavior Of Thermally Aged Austenitic Stainless Steel Weld

The structural integrity of stainless steel (SS) welds is of critical importance for the long-term service of light water reactors (LWRs).Exposed to corrosive reactor coolants and high service temperatures, SS welds are vulnerable to stress corrosion cracking (SCC) and thermal aging embrittlement.To...

Full description

Bibliographic Details

Published in:	NCSU Libraries Repository (North Carolina State University Libraries)
Main Author:	Yiren Chen
Other Authors:	Xu Chen, Yong Yao Yang, Chen Wy, Bogdan Alexandreanu, Krishnamurti Natesan, Rao Av
Format:	Article
Language:	English
Published:	North Carolina State University 2019
Subjects:	Hydrogen embrittlement and corrosion behaviors in metals Fatigue and fracture mechanics High Temperature Alloys and Creep austenitic stainless steel welds 304L stainless steel thermal aging stress corrosion cracking fracture toughness J-R curve crack growth rate weld metal
Online Access:	https://www.lib.ncsu.edu/resolver/1840.20/37570
Tags:	Add Tag No Tags, Be the first to tag this record!