Short/small fatigue crack growth, thresholds and environmental effects: a tale of two engineering paradigms

Abstract This paper results from mutual discussions on the review ‘When do small fatigue cracks propagate and when are they arrested?’ in Corrosion Reviews, 2019; 37(5): 397–418. These discussions have arisen from the two engineering paradigms characterizing our fatigue research: (i) an aerospace re...

Full description

Bibliographic Details

Published in:	Corrosion Reviews
Main Authors:	Russell J.H. Wanhill, Stefanie E. Stanzl‐Tschegg
Format:	Article
Language:	English
Published:	De Gruyter 2021
Subjects:	Fatigue and fracture mechanics Hydrogen embrittlement and corrosion behaviors in metals Material Properties and Failure Mechanisms short fatigue cracks fatigue crack growth fatigue crack growth threshold high cycle fatigue very high cycle fatigue fatigue design fatigue life prediction corrosion fatigue environmental effects on fatigue
Online Access:	https://www.degruyter.com/document/doi/10.1515/corrrev-2020-0096/pdf https://doi.org/10.1515/corrrev-2020-0096
Tags:	Add Tag No Tags, Be the first to tag this record!